VERBATIM 3D Printer Filament PET-G 1.75mm, 327m, 1kg black
Kód: 714058Skladem3ks
Termín a způsob doručení
Typ materiálu:PETG; Barva:Černá; Průměr struny:1,75 mm; Pracovní teplota:230 - 250°C; Balení:1 000 gramů.Více
/heart.svg){kind=small}
/compare.svg){kind=small}
Vyberte si zvýhodněné balení
Množstevní slevy
/envelope.svg){kind=small}
Dotaz
/bell.svg){kind=small}
Hlídat
/share.svg){kind=small}
Sdílet
Parametry
Výrobce:
Kód:
714058
EAN:
023942550525
Záruka:
24 Měsíc(ů)
Stav:
Barva:
Černá
Typ materiálu:
PETG
Průměr struny:
1,75 mm
Pracovní teplota:
230 - 250°C
Balení:
1 000 gramů
Popis VERBATIM 3D Printer Filament PET-G 1.75mm, 327m, 1kg black
Features
- Strong, high clarity, odour neutral and easy-to-print filament
- High impact strength
- Excellent flexibility
- Almost no warping or shrinkage
- Hydrophobic (does not absorb water)
- Food packaging grade pellets used
- Main applications: Concept modelling for mechanics, medical, food containers, transparent objects.
TECHNICAL SPECIFICATIONS
| Diameter | 1.75 mm ± 0.05 mm |
| Roundness | >95% |
| RAL | 9017 |
| Weight | 1000 g |
| Color | black |
| MATERIAL PROPERTIES | |
| Specific gravity | 1.27g/cc (Test method: ISO 1183) |
| MFR 190°C/2.16 kg | 6.4 gr/10 min (Test method: ISO 1133) |
| Tensile strength at yield | 50 mPa |
| Strain at yield | 5% (Test method: ISO 527) |
| Strain at break | 23% (Test method: ISO 527) |
| Tensile modulus | 2020 MPa (Test method: ISO 527) |
| Flexural modulus | 2050 MPa (Test method: ISO 178) |
| Flexural strength | 69 MPa (Test method: ISO 178) |
| Impact strength - Charpy method 23°C | 8.1 kJ/m2 (Test method: ISO 179) |
| Rockwell Hardness | 105 (Test method: ASTM D785) |
| Moisture absorption | 1104 ppm (Test method: ISO 62) |
| Printing temperature | 240±10°C |
| Heat deflection temperature | 70°C (Test metod: ASTM 648) |
| Transparency | 90% (Test method: ASTM D1003) |
.
, ,